Orfibrace Fracture Bracing And Immobilization Splinting Material
Orfibrace Fracture Bracing And Immobilization Splinting Material

Orfibrace Fracture Bracing And Immobilization Splinting Material

Brand/Manufacturer: ORFIT INDUSTRIES
Save
  • Latex Free

Orfibrace Fracture Bracing And Immobilization Splinting Material is ideal for medium to large splints, such as back supports, anti-spasticity upper extremity splints, body jackets and lower extremity orthoses. Orfibrace is used on patients who are unable to cooperate in the splinting process, such as those with abnormal tone conditions or joint contractures. Once fully molded, it becomes a rigid, supportive device that will not shrink after cooling. When heated, it initially has a slightly tacky surface, which helps the material stay in place for an intimate fit.

Item #DescPkgPrice 
NC13341 1/8" (3.2mm), Smooth, 24" x 36" (60 x 90cm) 2/Pack $452.97 $317.99
NC13343 1/8" (3.2mm), Perforated 1%, 24" x 36" (60 x 90cm) 2/Pack $521.58 $425.99

Features

  • Orfibrace Fracture Bracing And Immobilization Splinting Material can be stretched and pulled around curves without thinning or growing out of control
  • Tolerates heavy handling without showing fingerprints, leaving smooth, rounded edges
  • Provides professional looking image with glossy smooth gray finish
  • Moderate to maximum resistance to stretch
  • Can be handled firmly
  • Can be stretched and pulled around curves without thinning or growing out of control
  • Moderate drape
  • Offers good conformability for an intimate fit
  • Only moderate pressure is required to contour the material
  • Moderate to maximum memory
  • Material can be reheated to slowly return it to its original size
  • Moderate to Maximum rigidity
  • Splints will hold their shape against the pull of strong muscles or hypertonicity
  • When heated, it initially has a slightly tacky surface, which helps the material stay in place for an intimate fit
  • Pinch it together while warm to make a temporary bond
  • Apply solvent and dry heat to achieve a permanent bond
  • Resists fingerprints. 
  • Once fully molded, it becomes a rigid, supportive device that will not shrink after cooling
  • Sets up in three to six minutes at 150°F (66°C)
  • Density: 1.21 g cm³
  • Surface feeling: smooth
  • Color: grey
  • Odor: none
  • Biocompatible: Yes
  • Thickness: 3.0mm
  • Perforation: 1 % (macro)
  • Activation time (in water bath): 3 - 4 min
  • Working time: 1 - 1 1/2 min
  • Hardening time: 5 3/4 - 6 1/4 min
  • Time to completion: 22 - 23 min
  • Mechanical properties at 21°C (70°F)
    - Flexural modulus: 650MPa
    - Elastic modulus: 340 MPa
    - Tensile strength: 13.0 MPa
    - Strain at break: 60 %
    - Shore D hardness: 59
  • Maximum elongation when activated: 1800 %
  • Latex Free

Customer Reviews

Questions & Answers


 
 
Please enter your and your friends email address below.
Fields marked with * are compulsory
 
*
*
*
*

 
SubmitCancel
The selected product information has been successfully emailed to your friend.

Thank you for using www.healthproductsforyou.com

Close